| Customization: | Available |
|---|---|
| Type: | EP300 |
| Material: | Rubber |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Type | Textile Type | Strength Per Ply Min.(N/mm) | Plies of Fabric | Cover Thickness(mm) | Belt Width (mm) | Cover Grade | |
Top Cover | Bottom Cover | ||||||
EP Belt | EP-100 | 100 | 2-8 | 2-16 | 0-10 | 300-3400 | Abrasion resistant Impact resistant Heat resistant Oil resistant Acid/alkali resistant Fire resistant etc. |
EP-125 | 125 | ||||||
EP-150 | 150 | ||||||
EP-200 | 200 | ||||||
EP-250 | 250 | ||||||
EP-300 | 300 | ||||||
EP-350 | 350 | ||||||
EP-400 | 400 | ||||||
EP-500 | 500 | ||||||
NN Belt | NN-100 | 100 | 2-10 | ||||
NN-125 | 125 | ||||||
NN-150 | 150 | ||||||
NN-200 | 200 | ||||||
NN-250 | 250 | ||||||
NN-300 | 300 | ||||||
NN-400 | 400 | ||||||
NN-500 | 500 | ||||||
CC Belt | CC56 | 56 | 3-12 | ||||
Item | Type | ||||
NN, EP, CC | |||||
Adhesion strength | Between coating and belt cores | Thickness of coating layer more than 1.5mm ≥N/mm | 3.5 | ||
Thickness of coating layer 0.8~1.5mm More than N/mm | 3.2 | ||||
Between layers ≥N/mm | 4.5 | ||||
Tensile strength value of full thickness belt / N/mm | 160~3150 | ||||
Elongation of longitudinal reference force of full thickness belt / %≤ | 4 | ||||
Coating performance | H (sharp wear) | D (high wear) | L (moderate wear) | ||
Breaking strength / MPa ≥ | 24 | 18 | 15 | ||
Elongation at break / %≥ | 450 | 400 | 350 | ||
Abrasion / mm3 | 120 | 100 | 200 | ||
Aging text (70℃×168h) Median value of tensile strength and elongation | It shall not be less than 75% of the corresponding value before aging. | ||||