| Customization: | Available |
|---|---|
| Material: | Natural Rubber |
| Usage: | Industrial Rubber Slab, Industrial, Flooring, Printing, Rubber Floor Covering |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Natural Rubber Sponge Sheet is a type of rubber sheet made from natural latex, which is processed into a porous, flexible material. It is characterized by its high elasticity, resilience, and compressibility, making it ideal for applications that require cushioning or shock absorption. The sponge structure allows it to be lightweight while maintaining strength and durability, and it can be easily compressed or deformed under pressure but will return to its original shape once the pressure is released.
This type of rubber sheet is widely used in industries such as automotive, construction, electronics, and packaging, where it serves as a material for seals, gaskets, insulation, and cushioning. Its natural properties also provide resistance to wear, aging, and environmental factors, including ozone and UV exposure. Additionally, the high resilience of natural rubber sponge ensures long-lasting performance, even under frequent stress or compression.
Manufacturing natural rubber sponge sheets involves a process called foaming, where the latex is mixed with a foaming agent to create a cellular structure. The sheets can be customized in various thicknesses, densities, and colors to meet specific requirements. As a renewable and environmentally friendly material, natural rubber sponge sheets are a preferred choice for applications that demand both performance and sustainability.
Product Features:
Natural Rubber Sheet (NR): Experience unmatched flexibility and outstanding physical and mechanical properties.
SBR Rubber Sheet: Enjoy enhanced wear resistance and anti-aging features over NR, while being cost-effective.
Neoprene Rubber Sheet (CR): Renowned for its exceptional resistance to weather, ozone, heat, and harsh chemicals.
NBR (Nitrile) Rubber Sheet: Delivers superior oil resistance, wear durability, and anti-aging capabilities.
Other Rubber Sheet Options:
Choose from SBR, NBR/Nitrile, CR/Neoprene, EPDM Rubber Sheets
Silicone Rubber Sheet
| Property | Test Standard | Value |
| Polymer Type | Natural Rubber | |
| Hardness (Shore A) | ISO 868:2003 | 40 +/- 5 |
| Tensile strength (Mpa) | ISO 37:2017 | ≥22 |
| Elongation at break (%) | ISO 37:2017 | ≥700 |
| Tear Resistance (N/mm) | ISO 34-1:2015 | ≥60 |
| Abrasion Resistance at 5N (mm³) | ISO 4649:2017 | ≤60 |
| Density (g/cm³) | 1.05 +/- 0.05 | |
| Compression Set after 22h at 70ºC (%) | ISO 815-1:2014 | ≤30 |
| Operating Temperature (ºC) | -40ºC to 80ºC |
| Property | Test Standard | Value |
| Hardness change after 168h at 70ºC (Shore A) | ASTM D573-04(10) | ≤5 |
| Tensile strength change after 168h at 70ºC (%) | ASTM D573-04(10) | ≤-15 |
| Elongation at break change change after 168h at 70ºC (%) | ASTM D573-04(10) | ≤-25 |
| SBR | Working Temperature | -30°C-80°C | |
| Tensile strength | 2-8mpa | ||
| Hardness | 50-80 Duro | ||
| NBR | General Grade | High Grade | |
| Material Selection | SBR/NBR | Nitrile | |
| Working Temperature | -30°C-80°C | -30°C-110°C | |
| Tensile strength | 3-8mpa | ||
| Hardness | 50-80 Duro | ||
| CR | General Grade | High Grade | |
| Material Selection | SBR/CR | Neoprene | |
| Working Temperature | -30°C-80°C | -30°C-110°C | |
| Tensile strength | 3-8mpa | ||
| Hardness | 50-80 Duro | ||
| EPDM | General Grade | High Grade | |
| Material Selection | SBR/EPDM | EPDM | |
| Working Temperature | -30°C-80°C | -30°C-110°C | |
| Tensile strength | 3-8mpa | ||
| Hardness | 50-80 Duro | ||
| Silicone | Working Temperature | -50°C-220°C | |
| Tensile strength | 6-8mpa | ||
| Hardness | 60-70 Duro | ||
| Insulation | Polymer Content | 100% SBR | |
| Working Temperature | -30°C-100°C | ||
| Proof Voltage | 15KV-50KV | ||
| Color | Black, Grey | ||
| Surface | Smooth/ fine rib | ||
| Antistatic /ESD |
Material | NBR/SBR | |
| Working Temperature | -30°C-100°C | ||
| Top Layer | 107-109Ω | ||
| Bottom Layer | 103-105Ω | ||
| Color | Green+black | ||
){kind=link}