| Customization: | Available |
|---|---|
| Material: | Natural Rubber |
| Usage: | Industrial Rubber Slab, Industrial, Flooring, Printing, Rubber Floor Covering |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Fabric Waterproof EPDM Rubber Sheet
The insertion rubber sheet is ingeniously crafted by embedding cotton, nylon, or EP fabric within the rubber matrix. This design significantly enhances its anti-slip characteristics, coupled with superior abrasion resistance and remarkable impact strength. It is ideally suited for use as gaskets, seals, strips, and sealing strips in general construction, as well as for mounting pads across diverse industrial applications.
SBR Rubber Sheet:
This sheet offers outstanding wear resistance and surpasses natural rubber in its ability to withstand weather aging.
CR/Neoprene Rubber Sheet:
It delivers exceptional resistance to combustion, weather aging, and heat, along with admirable self-healing capabilities.
EPDM Rubber Sheet:
Known for its exceptional resistance to weather aging, ozone, polar liquids, and its remarkable waterproof properties.
NBR/Nitrile Rubber Sheet:
Renowned for its superior oil resistance, this sheet also excels in abrasion resistance, weather aging, and high-temperature endurance.
Main Features
Customization Options
| Property | Test Standard | Value |
| Polymer Type | Natural Rubber | |
| Hardness (Shore A) | ISO 868:2003 | 40 +/- 5 |
| Tensile strength (Mpa) | ISO 37:2017 | ≥22 |
| Elongation at break (%) | ISO 37:2017 | ≥700 |
| Tear Resistance (N/mm) | ISO 34-1:2015 | ≥60 |
| Abrasion Resistance at 5N (mm³) | ISO 4649:2017 | ≤60 |
| Density (g/cm³) | 1.05 +/- 0.05 | |
| Compression Set after 22h at 70ºC (%) | ISO 815-1:2014 | ≤30 |
| Operating Temperature (ºC) | -40ºC to 80ºC |
| Property | Test Standard | Value |
| Hardness change after 168h at 70ºC (Shore A) | ASTM D573-04(10) | ≤5 |
| Tensile strength change after 168h at 70ºC (%) | ASTM D573-04(10) | ≤-15 |
| Elongation at break change change after 168h at 70ºC (%) | ASTM D573-04(10) | ≤-25 |
| SBR | Working Temperature | -30°C-80°C | |
| Tensile strength | 2-8mpa | ||
| Hardness | 50-80 Duro | ||
| NBR | General Grade | High Grade | |
| Material Selection | SBR/NBR | Nitrile | |
| Working Temperature | -30°C-80°C | -30°C-110°C | |
| Tensile strength | 3-8mpa | ||
| Hardness | 50-80 Duro | ||
| CR | General Grade | High Grade | |
| Material Selection | SBR/CR | Neoprene | |
| Working Temperature | -30°C-80°C | -30°C-110°C | |
| Tensile strength | 3-8mpa | ||
| Hardness | 50-80 Duro | ||
| EPDM | General Grade | High Grade | |
| Material Selection | SBR/EPDM | EPDM | |
| Working Temperature | -30°C-80°C | -30°C-110°C | |
| Tensile strength | 3-8mpa | ||
| Hardness | 50-80 Duro | ||
| Silicone | Working Temperature | -50°C-220°C | |
| Tensile strength | 6-8mpa | ||
| Hardness | 60-70 Duro | ||
| Insulation | Polymer Content | 100% SBR | |
| Working Temperature | -30°C-100°C | ||
| Proof Voltage | 15KV-50KV | ||
| Color | Black, Grey | ||
| Surface | Smooth/ fine rib | ||
| Antistatic /ESD |
Material | NBR/SBR | |
| Working Temperature | -30°C-100°C | ||
| Top Layer | 107-109Ω | ||
| Bottom Layer | 103-105Ω | ||
| Color | Green+black | ||